We report the synthesis of room temperature (RT) stabilized γ–Bi2O3 nanoparticles (NPs) at the expense of metallic Bi NPs through annealing in an ambient atmosphere. RT stability of the metastable γ–Bi2O3 NPs is confirmed using synchrotron radiation powder X-ray diffraction and Raman spectroscopy. γ–Bi2O3 NPs exhibited a strong red-band emission peaking at ~701 nm, covering 81% integrated intensity of photoluminescence spectra. Our findings suggest that the RT stabilization and enhanced red-band emission of γ‒Bi2O3 is mediated by excess oxygen ion vacancies generated at the octahedral O(2) sites during the annealing process.
By using the numerical discretization method within the effective-mass approximation, we have theoretically investigated the exciton-related Raman scattering, interband absorption and photoluminescence in colloidal CdSe/CdS core/shell quantum dots ensemble. The interband optical absorption and photoluminescence spectra have been revealed for CdSe/CdS quantum dots, taking into account the size dispersion of the ensemble. Numerical calculation of the differential cross section has been presented for the exciton-related Stokes–Raman scattering in CdSe/CdS quantum dots ensemble with different mean sizes.
Zn2SiO4:Eu3+, Dy3+ phosphors have been prepared through the sol-gel process. X-ray diffraction (XRD), thermogravimetric and ddifferential thermal analysis (TG-DTA), FT-IR spectra and photoluminescence spectra were used to characterize the resulting phosphors. The results of XRD indicated that the phosphors crystallized completely at 1000oC. In Zn2SiO4:Eu3+,Dy3+ phosphors, the Eu3+ and Dy3+ show their characteristic red(613nm, 5D0-7F2), blue (481nm, 4F9/2–6H15/2) and yellow (577nm, 4F9/2–6H13/2) emissions.
Structural and Enhanced Optical Properties of Stabilized γ‒Bi2O3 Nanoparticles: Effect of Oxygen Ion Vacancies